In order to study the aging hardening characteristics and isothermal aging process of Ti-6Cr-5V-5Mo-4Al-1Nb alloy the time-temperature-transformation (TTT) curve of the alloy was measured by aging hardness method, and the microstructure changes during isothermal process were analyzed by XRD and SEM. It was found that the alloy had a high aging response speed at other aging temperatures except for the slow aging at 300°C and 400°C. When the aging time is prolonged at medium and low temperatures, the alloy can also produce the same aging strengthening effect as that at medium temperature aging, indicating that the temperature window of the alloy aging is wide, the aging strengthening effect is good, and it has the operability of heat treatment strengthening, so it is an ideal structural material. The isothermal aging transformation curve of the alloy is C type, and it can be obtained from the figure that the nose temperature is about 545°C
Subject
General Physics and Astronomy
Reference9 articles.
1. Quick reference guide for β titanium alloys in the 00s[J];Nyakana;Journal of Materials Engineering and Performance,2005
2. Perspectives on titanium science and technology[J];Banerjee;Acta Materialia,2013
3. The use of β titanium alloys in the aerospace industry[J];Boyer;(2005) Journal of Materials Engineering and Performance,2005
4. Determination of TTT curve of Ti-6554 titanium alloy [J];Li;Journal of Nonferrous Metals of China,2010