Structural and Optical Study of Oxygen Irradiated Rare Earth Doped Nickel Ferrite

Abstract

Abstract In present work, NiFe2O4 nanoparticles doped with 4% Ce ions were synthesized by chemical route using nitrates of iron, nickel and cerium with citric acid. Irradiation with swift heavy ions can modify the properties of ferrites significantly. Modification depends upon type of ion, energy and fluence used for irradiation. Presently NiCe0.04Fe1.96O4 sample was irradiated with 100 MeV O7+ beam at fluencies of 1×1012 ions/cm2, 5×1012 ions/cm2, 1×1013 ions/cm2 and 2×1013 ions/cm2. All samples (pristine and irradiated) were characterized by XRD, FTIR, Raman and UV-Vis spectroscopy. XRD patterns and FTIR spectra confirmed the spinel structure of sample. XRD parameters like crystallite size, lattice parameter, strain etc. were calculated, which show significant change only at the fluence of 5×1012 ions/cm2. UV-Vis spectra show two direct band gaps corresponding to low and high spin in all samples. Band gap was found to be higher for sample irradiated at 2×1013 ions/cm2 fluence in comparison to pristine sample. It is found that irradiation with 100 MeV oxygen affect the structural parameters in random way while optical band gap shows increasing trend with fluence.