Engineering of defects in fast neutron irradiated synthetic diamonds

Abstract

Abstract Chemical vapor deposited (CVD) diamonds have been irradiated with fast reactor neutrons at fluencies F = 1·1018 and 3 · 1018 cm-2 and then heated at temperatures up to 1600 °C. The processes of annealing in and annealing out of various complexes of intrinsic defects responsible for vibrational and electron-vibrational bands in the IR absorption spectra have been studied in detail. Some tens of local vibrational modes and zero-phonon lines with rather small width caused by numerous complexes of intrinsic defects were observed in the 400-11000 cm-1 range.