Narykova M V,Kadomtsev A G,Betekhtin V I,Kolobov Yu R,Dvorak J,Sklenicka V
Abstract
Abstract
This article considers the results of the study of the titanium VT1-0 surface degradation (Grade-4 equivalent) for recrystallized- and ultrafine-grained states after fatigue testing. Comparative analysis of peculiarities of the titanium samples degradation was performed after coating formation by Micro-Arc Oxidation. It was found, that the coating formed by Micro-Arc Oxidation shows different degradation behaviors for recrystallized and ultrafine-grained states