Physical and chemical properties of composite (Mo1-xNbx)Si2

Abstract

Abstract In this study, the effect of NbSi2 in the range from 10 to 90 wt% was investigated. on the properties of composites (Mo1-xNbx)Si2 obtained by hot pressing a solid-phase mixture of molybdenum and niobium disilicides at a temperature of 1700°C. Graphs of the dependence of density, bending strength, electrical resistivity, CLTE and microhardness of the content of NbSi2 were obtained. It was found, that with an increasing level of NbSi2 in the content, the flexural strength drops to 130 MPa. The electrical resistivity depending on the content of niobium silicide is extreme with a maximum for the composition (Mo0,5Nb0,5)Si2. In the concentration range of NbSi2 20-100 wt.% CLTE and microhardness of the composite within the error does not change.