Optimization of CF/PEKK molding process by orthogonal experiment

Abstract

Abstract Composite materials have gradually entered people’s attention due to their advantages such as lightweight, high strength, corrosion resistance, fatigue resistance, and strong designability. Widely used in aviation, aerospace, automotive and other fields.[1-4].. The basic mechanical properties of the laminates were evaluated through short beam shear and bending tests. The optimum forming process was determined by orthogonal test: forming temperature 380°C, forming pressure 2 MPa, holding time 60 min, cooling rate 2°C/min. The interlaminar shear strength of this process was 103.42 MPa, and the bending strength was 1570 MPa