Study of AC Susceptibility of La0.8Sr0.2MnO3 at Different Frequencies

Abstract

Abstract In the present work, the structural and ac magnetic susceptibility as a function of temperature at different frequencies of perovskite type La08Sr0.2MnO3 (LSMO) compound have been discussed. Conventional solid-state route was used to synthesize LSMO compound. Orthorhombic crystal structure with Pnma space group of the compound was witnessed from the analysis of X-ray diffractograms by Rietveld refinement. The real (χꞌ) and imaginary (χꞌꞌ) part of the ac susceptibility of the compound have been studied. The real part of magnetic susceptibility (χꞌ) of La0.8Sr0.2MnO3 sample increases as temperature decrease. This indicates that the paramagnetic-ferromagnetic phase transition occurs. At different frequencies, i.e. 100Hz and 500Hz the Curie temperature Tc are 326K and 336K respectively. Peaks observed in the imaginary part χꞌꞌ) of magnetic susceptibility plot indicate the presence of sample inhomogeneity.