Author:
Haleem Ali Hubi,Jamal Al-Deen Haydar H.J.,Shanan Ban Ahmed
Abstract
Abstract
The powder metallurgy (PM) method was used to create the alloy. The sintering process was carried out in an inert high-temperature tube furnace in the presence of inert gas at a temperature of 1000 ° C for 8 hours (Argon). In this article, the effect of (B) at three wt.% (0.4,0.8,1.2) on the corrosion rate, hardness, and microstructure of alloys was examined. X-ray diffraction (XRD), open circuit potential, electrochemical tests (Tafel extrapolation method), and Macro hardness Brinell were used to study the effect of adding (B) in various amounts to alloys. Saliva was utilized as the corrosion solution for the testing. The inclusion of the alloy element (B) increased hardness and a decrease in particle size, as seen by the microstructures. Furthermore, the corrosion resistance of the master alloy improved next the addition, as shown by Corrosion potential has increased while corrosion current densities have decreased. The corrosion rate for A, A1, A2 and A3 was 14.50, 7.42, 2.03and 2.77 (mpy) respectively.
Subject
General Physics and Astronomy
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献