4D printing and annealing of PETG composites reinforced with short carbon fibers

Author:

Rahmatabadi Davood,Soleyman Elyas,Fallah Min Bashi Mahshid,Aberoumand Mohammad,Soltanmohammadi Kianoosh,Ghasemi Ismaeil,Baniassadi MajidORCID,Abrinia Karen,Bodaghi MahdiORCID,Baghani MostafaORCID

Abstract

Abstract In this study, for the first time, post-heat treatment was applied to improve the stress recovery of short carbon fiber reinforced PETG (SCFRPETG). PETG and SCFRPETG composite were printed under optimal conditions, and constrained and free shape memory cycles were applied under compression and three-point bending loadings to assess shape and stress recovery. The results of the free shape memory test for both vertical and horizontal patterns showed that PETG composite also has a higher shape memory effect (SME) compared to PETG. The SME was significantly improved by performing heat treatment. The stress recovery values for pure PETG, reinforced PETG before and after annealing are 2.48 MPa, 3.04 MPa and 3.18 MPa, respectively. It showed that the addition of 1.5% carbon fiber increases the stress recovery by 22%. The increasing trend reaches 28% by performing post-heat treatment. Additionally, altering the printing pattern affects the programming and stress recovery values. For the SCFRPETG composite samples before and after annealing, changing the printing pattern from horizontal to vertical, resulted in a 16% and 7% increase in recovery stress, respectively. SEM results confirm that the annealing process removes the layered structure, micro-holes caused by shrinkage and 4D printing mechanism. Using the controlled heat treatment method can be a practical solution to solve the problem of adhesion and reduce the anisotropy of FDM 3D printed layers.

Publisher

IOP Publishing

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3