Magnetic and electrical transport properties of Cu0.5Ni0.5Fe2O4 ferrite synthesized by plasma arc discharge process

Abstract

Abstract In this study, the plasma arc discharge process was employed to synthesize nanocrystalline Cu0.5Ni0.5Fe2O4 ferrite powders. A spinel-type ferrite structure has been formed successfully, exhibiting a saturation magnetization of 87 emu g−1 and a coercivity of 26 Oe. The investigation involved studying the frequency and temperature dependence of dielectric permittivity, dielectric loss, and DC/AC conductivity over a broad frequency range (1 kHz–1 MHz) in a temperature range of 298 K–403 K. The highest value of the dielectric contestant (4746) is observed at a frequency of 1 kHz and temperature of 313 K. A maximum in the DC conductivity is observed at 403 K, which can be ascribed to the combined effects of thermally activated hopping and an increase in the concentration of both n-type and p-type charge carriers at higher temperatures.