Abstract
Abstract
The feasibility of a duplex coating based on cold spray technology and magnetron sputtering was evaluated for repair applications requiring a ‘thin-on-thick’ layered structure. Commercially pure angular-shaped Ti grade 4 particles are fed to a cold spray gun and accelerated toward a Ti alloy substrate to deposit thick coatings (∼4.5 mm). TiN and AlTiN thin films are deposited on polished cold spray coatings using a four-source closed-field unbalanced magnetron sputtering (CFUBMS) system. Microstructure was characterized using focused ion beam (FIB) lift-out, scanning electron microscopy (SEM), and electron channeling contrast imaging (ECCI). The nanoindentation technique was used to evaluate the mechanical properties of coatings. The H/E ratios and H3/E2 ratios for TiN films were found to be 0.098 and 0.26 GPa, respectively, while those for AlTiN films were measured at 0.066 and 0.052 GPa, respectively, suggesting higher capacity of TiN films to withstand both elastic and plastic deformation. Using scratch testing, the adhesion of TiN and AlTiN thin films to cold spray Ti was investigated, with TiN-Ti duplex coatings exhibiting better performance compared to AlTiN-Ti coatings. Tribological testing was performed on duplex coatings using a reciprocating tribometer equipped with an alumina ball counterface. The wear rate for AlTiN-Ti coatings after 2000 sliding cycles was found to be (1.0 × 10−3 ± 0.1 × 10−3 mm3/Nm), three orders of magnitudes higher than that for TiN-Ti (8 × 10−6 ± 2 × 10−6 mm3/Nm. SEM was used to reveal worn surface morphologies and cross-sectional analysis of the wear track. Subsurface microstructural changes due to wear were examined using focused ion beam cross-sectioning, revealing bending cracks and tribofilm formation.