Abstract
Abstract
The current study deals with the erosion behaviour of a plasma-sprayed 70% NiCrAlY + 30% TiO2 coating on MDN 420 steel substrate at extreme temperatures. The coating was characterized by using an optical microscope, Scanning Electron Microscopy and X-ray diffraction methods. The coating’s porosity, microhardness, surface roughness, and adhesion strength were all examined. The solid particle erosion experiments were carried out at temperatures of 300 °C, 500 °C, and 700 °C, with impact angles of 30° and 90°. The tests were conducted by using the alumina as an erodent in the hot air jet erosion testing machine. The erosion volume loss of coated and uncoated samples was measured using an optical profilometer. It is observed that erosion resistance of the coating was found to be more when compared to the substrate for the different test temperatures chosen. As the temperature increases, the erosion resistance of the coating also found increased from 300 °C to 700 °C at both impact angles of 30° and 90°. The morphology of the eroded coating surface reveals that the generalized behaviour of the coating is ductile in nature.
Funder
All India Council for Technical Education
Subject
Materials Chemistry,Surfaces, Coatings and Films,Process Chemistry and Technology,Instrumentation
Cited by
33 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献