Author:
Huang Lin-Ao,Wang Mei-Yu,Wang Peng,Yuan Yuan,Liu Ruo-Bai,Liu Tian-Yu,Lu Yu,Chen Jia-Rui,Wei Lu-Jun,Zhang Wei,You Biao,Xu Qing-Yu,Du Jun
Abstract
Abstract
The realization of perpendicular magnetization and perpendicular exchange bias (PEB) in magnetic multilayers is important for the spintronic applications. NiO(t)/[Ni(4 nm)/Pt(1 nm)]2 multilayers with varying the NiO layer thickness t have been epitaxially deposited on SrTiO3 (001) substrates. Perpendicular magnetization can be achieved when t < 25 nm. Perpendicular magnetization originates from strong perpendicular magnetic anisotropy (PMA), mainly resulting from interfacial strain induced by the lattice mismatch between the Ni and Pt layers. The PMA energy constant decreases monotonically with increasing t, due to the weakening of Ni (001) orientation and a little degradation of the Ni–Pt interface. Furthermore, significant PEB can be observed though NiO layer has spin compensated (001) crystalline plane. The PEB field increases monotonically with increasing t, which is considered to result from the thickness dependent anisotropy of the NiO layer.
Subject
General Physics and Astronomy
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献