Conversion of cassava rhizome into efficient carbonaceous adsorbents for removal of dye in water

Author:

Phuriragpitikhon J,Pluamjai K,Fuangchoonuch W,Chuenchom L

Abstract

Abstract The development of sustainable adsorbent materials for removing pollutants from water is of great interest for environmental remediation and human safety. This work presents the beneficial use of cassava rhizome (CR) to produce economical and efficient carbonaceous adsorbents for dye removal. CR derived activated carbons (AC) and magnetic AC were fabricated by one-pot hydrothermal carbonization in the presence of ZnCl2 and ZnCl2/FeCl3 respectively, followed by pyrolysis at 800 °C. Porosity tuning and degree of magnetization of as-prepared carbons were achieved by varying the amount of ZnCl2 and FeCl3 as an activating agent and source of magnetic particles respectively. The result indicated that the optimal condition to obtain ACs with a high SBET (1405 m2/g) and the largest mesopore volume (0.54 cm3/g) was using the weight ratio of ZnCl2 to CR of 3 (3AC). While, the magnetic mesoporous carbon with the highest SBET (554 m2/g) was yielded when addition of FeCl3 into the reaction mixture with a FeCl3 to ZnCl2 weight ratio of 1(3AC-1M). 3AC and 3AC-1M were tested as adsorbents to investigate the adsorption efficiency of methylene blue (MB) in water. The adsorption behavior of MB on 3AC and 3AC-1M were monolayer adsorption based on the Langmuir isotherm model with R2 of 0.9993 and 0.9953, respectively. 3AC showed the MB adsorption capacity of 274 mg/g which is comparable to that of commercial ACs. 3AC-1M that adsorbs MB with the maximum capacity of 102 mg/g, was separated from aqueous solution easily using an external magnet. This study demonstrates that the carbon precursors from biomass waste as CR can be conveniently converted into efficient carbonaceous adsorbents and functionalized for example by adding magnetic properties into the carbon structure to enable manipulations in industrial operations.

Publisher

IOP Publishing

Subject

General Engineering

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3