Guntur I N,Tjaronge M W,Irmawaty R,Ekaputri J J
Abstract
Abstract
This study discusses the effect of heating duration and curing age on compressive strength geopolymer paste made with medium calcium fly ash and potassium hydroxide solution (KOH). The hardening process was performed in an oven at a temperature of 100 ± 5°C in a variety of heating duration for 2, 4, and 6 hours to form a geopolymer paste with a potassium hydroxide concentration of 6 M. Flow testing on fresh paste indicatesd that all materials was bond properly without segregation. After the heating process in the oven, the spesimens were cured at room temperature until the age of 3, 7, and 28 days. The results of the compressive tests indicated that the heating duration and curing age were the key factors. Where there is no visible negative effect of the medium level CaO content in fly ash against compressive strength development of the hardened geopolymer paste.
Reference18 articles.
1. Environmentally Driven Geopolymer Cement Applications;Davidovits,2002
2. CCP Production and Use Survey,2014
3. Comparison of using NaOH and KOH Activated Fly Ash-based Geopolymer on the Mechanical Properties;Rahim;Material Science Forum,2015
4. The Mechanical Properties of Fly Ash-Based Geopolymer Concrete with Alkaline Activators;Ryu;Construction and Building Materials,2013
5. Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete,2005
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献