Abstract
Abstract
Glass fiber reinforced concrete (GFRC) is a very widely used material. However, the highly alkaline environment in concrete will erode and destroy the glass fiber therein, so it is particularly important to improve the corrosion resistance of glass. In this study, ZrO2 and TiO2 were introduced into the La2O3-CaO-Al2O3-P2O5 system glass and their effects on the structure and properties of the glass were systematically studied. The results show that the introduction of ZrO2 and TiO2 has a similar effect on rare earth doped glass. For one thing, it will increase the density of the glass and make the structure of the glass dense. For another, it can improve the water resistance and alkali corrosion resistance of the glass. SEM images showed that after the glass was immersed in the alkali solution, a protective CaO film was formed on the surface of the glass sample. As the etching time increases, the protective film on the glass surface peels off in a sheet shape, and the skeleton of the glass peels off in a lump shape.
Reference16 articles.
1. Improving the resistance of concrete panels to hard projectile impact;Abdel-Kader;International Journal of Protective Structures,2019
2. The Influence of Glass Fibers as Dispersed Reinforcement on Hydric Properties of Concrete;Pernicova;Solid State Phenomena,2016
3. Effect of seawater exposure on compressive behavior of concrete columns reinforced longitudinally with glass fiber reinforced polymer bars;Wei;Journal of Composite Materials,2018
4. Glass fibre reinforced precast concrete containing high content pozzolanic materials;Amed;Sigma Journal of Engineering and Natural Sciences-Sigma Muhendislik Ve Fen Bilimleri Dergisi,2019
5. Alkali-resistant glass fiber reinforced high strength concrete in simulated aggressive environment;Kwan;Materiales De Construction,2018
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献