Structural, electrical and dielectric properties of ZnFe2O4/Cu2S 3D heterostructures

Abstract

Abstract This work reports the fabrication of zinc ferrite-copper sulphide (ZnFe2O4/Cu2S) 3D heterostructures and subsequent investigation of the spectroscopic behaviour of various electrical parameters like conductivity, impedance and dielectric loss. The study reveals a non-monotonic behaviour of the real component of impedance (Z’), while the imaginary component of impedance (Z’) exhibits a temperature-dependent relaxation frequency, with an estimated activation energy (E a ) of 220.13 meV. The dc conductivity (σ dc ) measurements reveal the semiconducting nature of the sample and a transition from a ferrimagnetic to a paramagnetic behaviour is reported at the Curie temperature of 327 K. In case of ac conductivity (σ ac ), Jonscher’s power law σ ac = Aω n is followed and the exponent n is found to lie in the range 0.679–0.735 at different temperatures, which is best fitted into a polynomial of degree six. The temperature variation of n is suggestive of the overlapping large polaron tunnelling (OLPT) model. Further, ac activation energy (E ac ) is also calculated, which is found to be smaller than the dc activation energy (E dc ), indicating electron hopping between Fe3+ and Fe2+ ions. The numerically computed staying time (τ) of electrons in Fe3+/Fe2+ ionic sites varies with frequency as well as with temperature, ranging from 10−6s to 10−19s. A significant decrease in dielectric loss (tanδ) to the tune of 99% (from 75 at ∼100 Hz to 0.89 at ∼1 MHz) is reported at room temperature. In the present scenario, when smart materials like spinel ferrites have garnered significant attention for their promising magnetic and electric properties, our studies of the ZnFe2O4/Cu2S 3D heterostructures may provide immense possibilities for tailored applications in various electromagnetic applications.