Low-cycle fatigue (LCF) behavior of a novel near β titanium alloy Ti-6Mo-5V-3Al-2Fe (wt%) with various types of secondary α phase was investigated. Results indicate that No.1 microstructure containing crossed and fine intragranular α, as well as discontinuous GB α, is obtained through low temperature (480 °C) aging treatment. No.2 microstructure containing parallel and coarse intragranular α, as well as parallel WGB α, forms after high temperature (600 °C) aging treatment. Under all strain amplitudes, stress amplitudes and LCF life of the samples with No.1 microstructure are higher than those of the samples with No.2 microstructure. For the samples with No.1 microstructure, more and deeper secondary cracks and dimples form in fatigue crack propagation and fast fracture regions, respectively. Such fatigue fracture behavior reflects a longer LCF life.
Funder
Foundation of state key laboratory of rolling and automation, northeastern university
Liaoning provincial natural science foundation
Subject
Metals and Alloys,Polymers and Plastics,Surfaces, Coatings and Films,Biomaterials,Electronic, Optical and Magnetic Materials
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献