Three different metamaterial structures were fabricated using stereolithography 3D printing and a shape recovering material. Mechanical properties and recovery efficiency were assessed after compression testing. All three structures exhibited similar initial specific compressive moduli, while the highest specific toughness was observed for the stretch-dominated structure. The three metamaterial structures were re-tested after shape recovery. Significant strengthening was observed for all structures, with the bend-stretch-dominated structure strengthening to the highest degree. This strengthening phenomenon was characterized as strain hardening. It was found that the strengthening is highly geometry dependent. The geometry with stretch-dominated behavior exhibited the highest mechanical properties after a second test was performed. Improvements in specific toughness of up to 67% were observed after the second compressive test.
Subject
Metals and Alloys,Polymers and Plastics,Surfaces, Coatings and Films,Biomaterials,Electronic, Optical and Magnetic Materials
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献