Influence of boric anhydride reinforcement on mechanical properties and abrasive wear of nylon 6

Abstract

Abstract To investigate the influence of boric anhydride (B2O3) on mechanical properties of nylon 6, tensile, hardness and impact test were carried out. Average tensile strength along with percentage elongation and modulus of elasticity has been calculated and plotted in this paper. Rockwell hardness and Izod impact tests were carried out to identify the hardness and toughness of materials. Boric anhydride used in this research was limited to less than 10 wt% of nylon 6 matrix material and was 2 wt%, 4 wt% and 8 wt%. Abrasion resistance of pure nylon 6 and composites was measured as weight loss due to abrasion. For the characterization of nylon 6 and its composites, Thermo-gravimetric analysis (TGA) and x-ray diffraction (XRD) were carried out. In results, it was found that the boric anhydride reinforcement increased the tensile strength and abrasion resistance when used up to 2 wt% in the nylon 6 matrix. Hardness found to be continually increased as the boric anhydride reinforcement percentage increased. The crystallinity of nylon 6 was little affected due to fillers and was found minimum for the 4 wt% boric anhydride reinforced nylon 6 composites. It was also found that the elastic modulus, Rockwell hardness and tensile strength, abrasion resistance show good correlations which are discussed in the discussion section.