The behavior of hydrothermally synthesized hematite nanorods prepared on spin coated seed layers

Abstract

Abstract Herein we report on the effect of varied spin-coated seed layer concentrations of Iron (III) chloride hexahydrate (FeCl3.6H2O) on the photoelectrochemical performance of hydrothermally synthesized hematite nanorods. The seed layers were prepared from 0.05, 0.07, 0.09, 0.11, and 0.13 M concentrations of FeCl3.6H2O. The nanorods were vertically aligned with slight inclinations over the seed layers with the two lowest molar concentrations (0.05 and 0.07 M) of FeCl3.6H2O. A further increase in seed layer concentrations transformed the nanorods as they grew over others and agglomerated into clusters. Structural analysis using x-ray diffraction (XRD) and Raman spectroscopy demonstrated uniform hematite crystalline peaks for all the samples. All samples absorbed highly in the visible region within an onset absorption edge wavelength ranging from 624 to 675 nm. Overall, the nanorods synthesized over the lowest seed layer concentration of 0.05 M of FeCl3.6H2O exhibited the highest photocurrent density of 0.077 mA cm−2 at 1.5 V versus reversible hydrogen electrode. The results obtained provide important information about the structural, optical, and photoelectrochemical properties of hematite nanorods synthesized over varied seed layer concentrations. This is a key contribution in understanding and enhancing the hematite nanorods performance for photocatalytic applications.