Abstract
Abstract
Attaining low-temperature sintering and high electrical conductivity is vital in the field of flexible electronics. Inks with silver oxalate as the precursor have recently received significant attention in this field; however, the high sintering temperature and long sintering time limit commercial applicability. High sintering temperature can shorten the sintering time but lead to porous and uneven film morphology; thus, reducing the conductivity. On the other hand, low sintering temperature prolongs the sintering time; thus, reducing the production efficiency. To solve the abovementioned problems, a silver composite conductive ink modified by polyvinylpyrrolidone (PVP) was prepared in this study. The ink used silver oxalate as the precursor, methanol and acetone as the solvent, and 1, 2-diaminopropane as the complexing agent, and could reduce the sintering temperature and time to 160 °C and 20 min, respectively. After sintering, the silver film showed good electrical conductivity, and low resistivity (4.56 μΩ·cm). Furthermore, the impact of sintering temperature on the surface morphology and electrical conductivity were also studied, and the results showed that PVP had a positive influence on the nucleation of silver and the microstructure of the sintered silver film.
Funder
National Natural Science Foundation of China
Technology Projects of Yunnan Province
Subject
Metals and Alloys,Polymers and Plastics,Surfaces, Coatings and Films,Biomaterials,Electronic, Optical and Magnetic Materials
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献