Effect of heat treatment process parameters on the microstructure and properties of GH4720Li superalloy

Author:

Wei ZhangORCID,Jingnan Li,Ruifeng Dong,Zishuai ChenORCID,Jian Li,Xing Zhou,Qingzeng Wang,Jinglong Qu

Abstract

Abstract The solution temperature and aging temperature of GH4720Li superalloy are the critical factors in determining its microstructure stability and mechanical properties. However, the matching of solution temperature, primary aging temperature, and second aging temperature greatly influences the final microstructure and mechanical properties, and the mechanism was rarely studied. In this paper, the effects of solution temperature, aging temperature, and other process parameters on the grain size, precipitated phase, and mechanical properties of GH4720Li superalloy were systematically studied by orthogonal experiment, and a set of optimal heat treatment process parameters were found. The results show that the sample was solution treated in the temperature range of 1060 °C ∼ 1120 °C. When the solution temperature was 1160 °C ∼ 1100 °C, although the primary γ ′ phase gradually dissolved, the secondary γ ′ phase gradually increased, and the primary γ ′ phase was pinned at the grain boundary to hinder the grain growth, and the hardness of the alloy gradually increases. When the solution temperature exceeded 1100 °C, the primary γ ′ phase dissolved in large quantities, the grains grew up rapidly, and the hardness of the alloy decreased. The sample was subjected to two-stage aging treatment in the temperature range of 650 °C ∼ 770 °C and 760 °C ∼ 880 °C. As the aging temperature increased, the primary γ ′ phase of the sample gradually grew, and the ability to pin the grain boundary weakened. The volume fraction of the secondary γ ′ phase of the sample gradually decreased and coarsened, resulting in grain growth and a gradual decrease in the hardness of the sample. When the samples were treated by 1100 °C/OC × 4 h + 650°C /AC × 8 h + 760 °C/AC × 8 h, the grain size of the sample was the smallest, the average grain size was 4.5 μm, the distribution of γ ′ phase was the most uniform, and the mechanical properties are the best, reaching 47 HRC.

Funder

Inner Mongolia University of Technology 2022 Undergraduate Science and Technology Innovation Fund Project

The science and technology plan project of Inner Mongolia

Basic Scientific Research Expenses Program of Universities directly under Inner Mongolia Autonomous Region

Publisher

IOP Publishing

Subject

Metals and Alloys,Polymers and Plastics,Surfaces, Coatings and Films,Biomaterials,Electronic, Optical and Magnetic Materials

Reference26 articles.

1. Hot deformation behaviors and microstructure evolution of GH4049 alloy;Li;J. Mater. Eng.,2014

2. Influence of processing parameters on dynamic recrystallization and the associated annealing twin boundary evolution in a nickel base superalloy;Pradhan;Mater. Sci. Eng. A,2017

3. Cooling precipitation and strengthening study in powder metallurgy superalloy U720LI;Mao;Metallurgical & Materials Transactions a,2001

4. γ′-(L12) precipitate evolution during isothermal aging of a CoAlWNi superalloy;Sauza;Acta Mater.,2019

5. Microstructure and phase precipitate behavior of Inconel 740H during aging;Guo;Transactions of Nonferrous Metals Society of China,2016

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3