Investigation on surface roughness of sintered PA2200 prototypes using Taguchi method

Abstract

Purpose The purpose of this research paper is to optimize the process parameters of selective laser sintering process, and the sintered parts of PA2200 prototypes are built with minimum surface roughness within the range of 10-12 microns using the Taguchi design of experiments approach. Design/methodology/approach In this research paper, a 3D model is created using catia V5 and exported to rapid prototype machine, and the 3D model file was repaired by using Magics software to remove the facets and saved with file extension .stl (standard triangulation language).Taguchi design of experiments approach L9 orthogonal array was selected with three factors at three levels each and total nine experiments were conducted with the quality index lower-the-better signal-to-noise ratio to produced better quality prototypes by optimizing the process parameters like laser power, layer thickness and temperature and tested on surface tester for surface roughness. The experimental results of surface roughness were compared with Regression Analysis, S/N Ratio, Analysis of Mean and predicted model on sintered prototypes. Findings The experimental results obtained after testing on the surface tester compared with mathematical model for the quality index lower-the-better signal-noise ratio with optimal process parameters operating at Temperature at level 3, Layer thickness at level 3, and Laser power at level 3, regression analysis, and predictive model the output response variable surface roughness, is with in the range of 9-10.5 microns are all most same and from ANOM (Analysis of Mean), temperature at leve1, layer thickness at level 2, laser power at level 2 is 9 -9.6 microns. Research limitations/implications The process parameters such as beam diameter and table speed were not considered on output response variable surface roughness in this research paper. Originality/value All the experiments were conducted and the parts are produced by using the material PA2200 in the powder from and sintered by Co2 laser by varying the process parameters with optimal settings to produce minimum surface roughness the out put from this paper is the influence of process parameters on surface roughness can be predicted at optimal settings with in less time and cost.