Abstract
PurposeThe purpose of this study is to explore the feasibility of utilizing agricultural (almond shell, rice husk and wood) waste biochars for partial cement replacement by evaluating the relationships between the physiochemical properties of biochars and the early-age characteristics of cement pastes.Design/methodology/approachBiochars are prepared through the thermal decomposition of biomass in an inert atmosphere. Using varying percentages, biochars are used to replace ordinary Portland cement (OPC) in cement pastes at a water/binder ratio of 0.35. Characterization methods include XPS, FTIR, SEM, TGA, BET, Raman, loss-on-ignition, setting, compression and water absorption tests.FindingsAccelerated setting in biochar-modified cement pastes is attributed to chemical interactions between surface functional groups of biochars and calcium cations from OPC, leading to the early development of metal carboxylate and alkyne salts, alongside the typical calcium-silicate-hydrate (C-S-H). Also, metal chlorides such as calcium chlorides in biochars contribute to the accelerate setting in pastes. Lower compression strength and higher water absorption result from weakened microstructure due to poor C-S-H development as the high carbon content in biochars reduces water available for optimum C-S-H hydration. Amorphous silica contributes to strength development in pastes through pozzolanic interactions. With its optimal physiochemical properties, rice-husk biochars are best suited for cement replacement.Research limitations/implicationsWhile biochar parent material properties have an impact on biochar properties, these are not investigated in this study. Additional investigations will be conducted in the future.Practical implicationsCarbon/silicon ratio, oxygen/carbon ratio, alkali and alkaline metal content, chlorine content, carboxylic and alkyne surface functional groups and surface areas of biochars may be used to estimate biochar suitability for cement replacement. Biochars with chlorides and reactive functional groups such as C=C and COOH demonstrate potential for concrete accelerator applications. Such applications will speed up the construction of concrete structures and reduce overall construction time and related costs.Social implicationsReductions in OPC production and agricultural waste deterioration will slow down the progression of negative environmental and human health impacts. Also, agricultural, manufacturing and construction employment opportunities will improve the quality of life in agricultural communities.Originality/valueEmpirical findings advance research and practice toward optimum utilization of biomass in cement-based materials.
Subject
Building and Construction,Civil and Structural Engineering
Reference93 articles.
1. Physico-mechanical properties of composite cement pastes containing silica fume and fly ash;Housing and Building National Research Center,2015
2. Novel bio-char-concrete composites: manufacturing, characterization, and evaluation of the mechanical properties;The Science of the Total Environment,2018
3. American Society for Testing and Materials (2016), “ASTM C109/C109M-16a, standard test method for compressive strength of hydraulic cement mortars (using 2-in. Or [50- mm] cube specimens)”, available at: https://www.astm.org/Standards/C109.htm (accessed 26 March 2020).
4. American Society for Testing and Materials (2019a), “ASTM C188-17, standard test method for density of hydraulic cement”, available at: https://www.astm.org/Standards/C188 (accessed 26 March 2020).
5. American Society for Testing and Materials (2019b), “ASTM C191-19, standard test methods for time of setting of hydraulic cement by Vicat Needle”, available at: https://www.astm.org/Standards/C191 (accessed 26 March 2020).
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献