High temperature erosion behavior of plasma sprayed Al2O3 coating on AISI-304 stainless steel

Author:

Prashar Gaurav,Vasudev Hitesh

Abstract

Purpose In the present study, Al2O3 coatings were deposited on stainless steel AISI-304 material by using atmospheric plasma spraying technique to combat high temperature solid particle erosion. The present aims at the performance analysis of Al2O3 coatings at high temperature conditions. Design/methodology/approach The erosion studies were carried out at a temperature of 400°C by using a hot air-jet erosion tester for 30° and 90° impingement angles. The possible erosion mechanisms were analyzed from scanning electron microscope (SEM) micrographs. Surface characterization of the powder and coatings were conducted by using an X-ray diffractometer, SEM, equipped with an energy dispersive X-ray analyzer. The porosity, surface roughness and micro-hardness of the as-sprayed coating were measured. This paper discusses outcomes of the commonly used thermal spray technology, namely, the plasma spray method to provide protection against erosion. Findings The plasma spraying method was used to successfully deposit Al2O3 coating onto the AISI 304 substrate material. Detailed microstructural and mechanical investigations were carried out to understand the structure-property correlations. Major findings were summarized as under: the erosive wear test results indicate that the plasma sprayed coating could protect the substrate at both 30° and 90° impact angles. The coating shows better resistance at an impact angle of 30° compared with 90°, which is related to the pinning and shielding effect of the alumina particle. The major erosion wear mechanisms of Al2O3 coating were micro-cutting, micro-ploughing, splat removal and detachment of Al2O3 hard particles. Originality/value In the current study, the authors have followed the standard testing method of hot air jet erosion test as per American society for testing of materials G76-02 standard and reported the erosion behavior of the eroded samples. The coating was not removed at all even after the erosion test duration i.e. 10 min. The erosion test was continued till 3 h to understand the evolution of coatings and the same has been explained in the erosion mechanism. The outcome of the present study may be used to minimize the high temperature erosion of AISI-304 substrate.

Publisher

Emerald

Subject

Electrical and Electronic Engineering,Mechanical Engineering,Mechanics of Materials,Geotechnical Engineering and Engineering Geology,Civil and Structural Engineering

Cited by 63 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3