Fabrication and compressive properties of Ti6Al4V implant with honeycomb‐like structure for biomedical applications
Author:
Li Xiang,Wang Chengtao,Zhang Wenguang,Li Yuanchao
Abstract
PurposeThe purpose of this paper is to verify the feasibility and evaluate the compressive properties of Ti6Al4V implants with controlled porosity via electron beam melting process. This process might be a promising method to fabricate orthopedic implants with suitable pore architecture and matched mechanical properties.Design/methodology/approachTi6Al4V implants with controlled porosity are produced using an electron beam melting machine. A scanning electron microscope is utilized to examine the macro‐pore structures of the Ti6Al4V implants. The compressive test is performed to investigate the mechanical properties of the porous implants.FindingsThe fabricated samples show a fully interconnected open‐pore network. The compressive yield strength of the Ti6Al4V implants with the porosity of around 51 percent is higher than that of human cortical bone. The Young's modulus of the implants is similar to that of cortical bone.Research limitations/implicationsThe surface of samples produced by electron beam melting process is covered with loosely spherical metal particles. Polishing and ultrasonic cleaning have to be used to remove the loose remnants.Originality/valueThis paper presents the potential application in the fabrication of orthopedic or dental implants using electron beam melting process.
Subject
Industrial and Manufacturing Engineering,Mechanical Engineering
Reference18 articles.
1. Collier, D.P., Mayor, M.B. and Chae, J.C. (1998), “Macroscopic and microscopic evidence of prosthetic fixation with porous‐coated materials”, Clin. Orthop., Vol. 3, pp. 249‐62. 2. Hollander, D.A., von Walter, M., Wirtz, T., Sellei, R., Schmidt‐Rohlfing, B., Paar, O. and Erli, H. (2006), “Structural, mechanical and in vitro characterization of individually structured Ti‐6Al‐4V produced by direct laser forming”, Biomaterials, Vol. 27, pp. 955‐63. 3. Hutmacher, D.W., Sittinger, M. and Risbud, M.V. (2004), “Scaffold‐based tissue engineering: rationale for computer‐aided design and solid free‐form fabrication systems”, Trends Biotechnol, Vol. 22 No. 7, pp. 354‐62. 4. Imwinkelried, T. (2007), “Mechanical properties of open‐pore titanium foam”, J Biomed Mater Res, Vol. 81, pp. 964‐70. 5. Kienapfel, H., Sprey, C., Wilke, A. and Griss, P. (1999), “Implant fixation by bone ingrowth”, J Arthroplasty, Vol. 14, pp. 355‐68.
Cited by
59 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献
|
|