Hot corrosion behaviour of CNT-reinforced ZrO2-Y2O3 composite coatings on boiler tube steel at 900°C

Author:

Kumar Sandeep,Bhatia Rakesh,Singh Hazoor

Abstract

Purpose In Indian thermal power plants, the main cause of boiler tube failure is the presence of molten sulphates and vanadates, which deteriorate the tube material at high temperatures. To combat the hot corrosion failure of metals, thermal spray technology is adopted. This study aims to investigate and study the effect of hot corrosion behaviour of carbon nanotube (CNT)-reinforced ZrO2-Y2O3 composite coatings on T-91 boiler tube steel in a molten salt environment at 900 °C for 50 cycles. Design/methodology/approach A plasma spray technique was used for development of the coatings. The samples were exposed to hot corrosion in a silicon tube furnace at 900 °C for 50 cycles. After testing, the test coupons were analysed by X-ray diffraction, scanning electron microscopy/energy dispersive spectroscopy and cross-sectional analysis techniques to aid understanding the kinetics of the corrosion reaction. Findings CNT-based reinforced coatings showed lower weight gain along with the formation of protective oxide scales during the experimentation. Improvement in protection against hot corrosion was observed with increase in CNT content in the coating matrix. Originality/value It is pertinent to mention here that the high temperature behaviour of CNT-reinforced ZrO2-Y2O3 composite on T-91 steel at 900°C temperature in molten salt environment has never been studied. Thus, the present research was conducted to provide useful results for the application of CNT-reinforced composite coatings at elevated temperature.

Publisher

Emerald

Subject

General Materials Science,General Chemical Engineering

Cited by 4 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3