Multilayer thick-film thermoelectric microgenerator based on LTCC technology

Abstract

Purpose The purpose of this paper was to develop the methodology of thick-film/low temperature co-fired ceramic (LTCC) multilayer thermoelectric microgenerator fabrication including the procedure of silver-nickel thermocouples integration with LTCC. Design/methodology/approach To miniaturize the structures and to increase the output parameters (generated voltage, electrical power), the microgenerator was designed as multilayer systems. It allows to reduce size of the system and to increase the number of thermocouples integrated inside the structure. It also protects buried thermocouples against exposure to harmful external factors (e.g. moisture, oxidation and mechanical exposures). As a substrate, LTCC was used. For the thermocouples fabrication, thick-film pastes based on silver and nickel were chosen. Ag/Ni thermocouple has nearly three times higher Seebeck coefficient and 30 per cent lower electrical resistance than the combination of Ag/PdAg used in previous works of the author. Findings A multi-layer thick-film thermoelectric generator based on LTCC and Ag, Ni pastes was fabricated. Thirty Ag/Ni thermocouples were precisely screen-printed on few layers. Thermocouples’ arms are 15 mm long and about 150 μm wide. Interlayer connections (via-holes filled with conductive paste) provided the electrical contact between the layers. The biggest fabricated harvester consisted of 90 miniature thermocouples buried inside the LTCC. Originality/value The paper presents the results of research that provided to optimize the co-firing process of the LTCC/Ni set. In the result, the methodology of co-firing of silver-nickel thermocouples and LTCC ceramic was elaborated. Also, the methodology of fabrication of miniature thermoelectric energy harvesters was optimized.