Mechanical, water absorption and thermal properties of kenaf fiber composite hybridized with Acacia concinna pods powder

Abstract

Purpose This study aims to investigate the mechanical, thermal and water absorption (WA) properties of kenaf fiber (KF) composites hybridized with powdered Acacia concinna pods (ACP). Design/methodology/approach Kenaf fiber reinforced epoxy polymer hybrid composite was fabricated using several weight percentages of ACP powder as filler (0%, 2%, 4%, 6% and 8%), both with and without chemically altering the fiber mat. 6 Wt.% NaOH was used in distilled water to treat KF mat chemically. The hand layup technique is used to produce ASTM-compliant KF hybrid laminates. Tensile, flexural and IZOD impact strengths were tested on the generated hybrid composites and their thermal and WA characteristics. Scanning electron microscope fractography revealed that fiber pulling-out, debonding and cracking were the main ways composites fractured. Findings The investigation findings reveal that the tensile, flexural and impact strengths increased when ACP fillers were added up to 4, 6 and 8 Wt.%, respectively. Thermogravimetric analysis indicates that the hybrid composite is thermally stable up to 215°C. WA experiments reveal that KF mat composites treated with 0 Wt.% ACP filler had less WA than those not treated with ACP filler. The treated KF with 4% filler hybrid composite demonstrated improved interfacial bonding between the reinforcement and matrix compared to other combinations. Originality/value Although filler made of A. concinna is inexpensive, lightweight, renewable, totally or partially recyclable and biodegradable, its potential application in hybridizing composites is yet to be investigated. Hybridizing the KF mat with ACP filler in an epoxy matrix produced novel hybrid composites. Evaluations have been conducted on the effects of ACP filler on the mechanical, thermal and WA characteristics of composites.