Author:
Abdeen Dana H.,Palmer Bruce R.
Abstract
Purpose
This paper aims to study the effect of processing parameters of an electron beam melting (EBM) machine on the surface roughness, critical pitting temperature and density of Ti-6Al-4V parts produced from the EBM machine.
Design/methodology/approach
In this study, statistically designed experiments were used to manufacture Ti-6Al-4V samples in the EBM machine under different process parameters of beam current, beam speed and offset focus. Surface roughness was measured for as-built samples using a 3D profilometer. Then, a potentiostatic test was conducted under 2.40 V vs saturated calomel electrode to determine the critical pitting temperature (CPT) in 3.5 per cent mass NaCl solution for the samples of different processing parameters. Next, density was measured for these samples. Finally, model equations were established to relate EBM’s process parameters to measured properties of surface roughness, CPT and density.
Findings
Results showed that offset focus had the main influence on surface roughness more than the beam current and the beam speed. Changing processing parameters did not affect corrosion behavior of EBM Ti-6Al-4V as CPT did not vary widely, although a slight effect on CPT values obtained from the beam current and the beam speed. Density was greatly affected by the offset focus more than the other parameters. It can be concluded that uniform and precise measurements of roughness and density are not achievable through this machine; only a range of these properties can be attained.
Originality/value
EBM machine produces 3D parts in a layer-based building process under high temperature and vacuum atmosphere. Due to the manufacturing technique and conditions, the resulting object has irregularities on the exterior surface and voids that are formed within the part, both of which affect samples’ properties like surface roughness, CPT and density. This study established model equations that can relate parts’ properties to processing parameters so that parts of specific properties are obtained to fit the application they are used for. For each property, ANOVA fits vs linear energy were also obtained.
Subject
Industrial and Manufacturing Engineering,Mechanical Engineering
Reference31 articles.
1. Corrosion behavior of Ti-6Al-4V alloy in different media;Al-Khawarizmi Engineering Jouranl,2010
2. Arcam (2013), “Arcam A2: Products: Arcam”, available at: www.arcam.com/arcam-a2/ (accessed July 2013).
Cited by
18 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献