Abstract
PurposeAlthough separate studies on the influence of corrosion and fire exposure on the constitutive relationship of concrete and steel have been done, there is still a gap in knowledge on the influence of corrosion-temperature superimposition as nonlinear phenomenon. The current study is focused to investigate the response of hot-rolled steel bars subjected to corrosion-temperature superimposition.Design/methodology/approachUsing the accelerated corrosion-impressed-current technique, hot-rolled specimens with different levels of corrosion were obtained. The hot-rolled rebars were first corroded to target levels such as (6, 12, 18, 24, 30 and 36%) and subsequently subjected to target temperatures (250 °C, 400 °C, 550 °C, 800 °C and 950 °C), before tensile tests were carried out to evaluate the residual mechanical response.FindingsThe outcomes showed a significant decline in the parameters governing the mechanical properties of steel reinforcement due to the combined damage due to corrosion and fire. Corroded reinforcement still showed ductile failure after exposure to fire. Moreover, the combined loss of load-bearing characteristics due to corrosion and fire has little influence on the modulus of elasticity. The outcomes of this investigation provide a theoretical database for the assessment of aged structural elements exposed to combination after exposure to fire.Originality/valueThe information concerning structural material's response to corrosion-temperature combined damage is still limited. The cover of the reinforcement is designed to safeguard the reinforcing bars from foreign agencies but is often damaged and spalled off due to corrosion, rendering the reinforcing bars directly exposed. The study aims at the experimental production of fire conditions in a corrosion-damaged infrastructure to cover the aforementioned research gap. The effects of corrosion being superimposed by exposure to elevated temperatures on key parameters affecting mechanical behavior were examined.HighlightsInfluence of corrosion-temperature superimposition on the mechanical properties of hot-rolled rebars.Influence of corrosion-temperature superimposition on the macro and microstructure properties of hot-rolled rebars.Influence of corrosion-temperature superimposition on stress-strain curves of hot-rolled rebars.Influence of corrosion-temperature superimposition on tensile strength, modulus of elasticity and elongation of hot-rolled rebars.