PAN Bazlı Nanofiberlerin Elektroeğirme ile Üretiminde Proses Değişkenlerinin İstatistiksel Modellenmesi
Author:
AYDIN Ebubekir Sıddık1ORCID, KORKUT İbrahim1
Affiliation:
1. Sivas Bilim ve Teknoloji Üniversitesi
Abstract
In this study, the effects of the electrospinning operating parameters such as flow rate (1-5 ml/h), voltage (15-30 kV), and distance to the collector (100-200 mm) on the physical properties of PAN-based nanofibers were investigated statistically by applying the central composite design method. The minimum nanofiber diameter was found to be 366.5 nm, under operating conditions of 5 ml/h flow rate, 30 kV, and 100 mm distance to the collector. Experimental conditions of 15 kV, 5 ml/h flow rate, and a 200 mm distance to the collector, a maximum porosity value of 0.446 was obtained. Similarly to the porosity, the water absorption capacity (WAC) value did not show a linear increase, and the maximum absorption capacity was calculated as 5712%, and at that point where the diameter is relatively large and the porosity is low.
Publisher
Politeknik Dergisi
Subject
Colloid and Surface Chemistry,Physical and Theoretical Chemistry
Reference25 articles.
1. [1] Choi, D., Kil, H.S., Lee, S., “Fabrication of low-cost carbon fibers using economical precursors and advanced processing technologies”, Carbon, 142, 610–649, (2019). 2. [2] Zabihi, O., Ahmadi, M., Li, Q., Shafei, S., Huson, M.G., Naebe, M.: Carbon fibre surface modification using functionalized nanoclay, “A hierarchical interphase for fibre-reinforced polymer composites”, Composites Science and Technology, 148, 49–58, (2017). 3. [3] Atlı İ.S. and Evcin A., “Analysing mechanical behaviors of carbon fiber reinforced silicone matrix composite materials after static folding”, Journal of Polytechnic, 23(2): 351-359, (2020). 4. [4] Huang, M., Tu, H., Chen, J., Liu, R., Liang, Z., Jiang, L., Shi, X., Du, Y., Deng, H., “Chitosan-rectorite nanospheres embedded aminated polyacrylonitrile nanofibers via shoulder-to-shoulder electrospinning and electrospraying for enhanced heavy metal removal”, Applied Surface Science, 437, 294–303, (2018). 5. [5] Chaúque, E.F.C., Dlamini, L.N., Adelodun, A.A., Greyling, C.J., Catherine Ngila, J., “Modification of electrospun polyacrylonitrile nanofibers with EDTA for the removal of Cd and Cr ions from water effluents”, Applied Surface Science, 369, 19–28, (2016).
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献
|
|