Adjustment of a technology of cast iron smelting in the blast furnace of jsc "ural steel" w ith a volume of 1232 см<sup>3</sup> with charge h a v in g 95% share of Mikhailovskii GOK pellets-Reference-Cited by-同舟云学术

Adjustment of a technology of cast iron smelting in the blast furnace of jsc "ural steel" w ith a volume of 1232 см³ with charge h a v in g 95% share of Mikhailovskii GOK pellets

Published:2021-08-01 Issue:7 Volume:77 Page:768-775
ISSN:2619-0753
Container-title:Ferrous Metallurgy. Bulletin of Scientific , Technical and Economic Information
language:
Short-container-title:Černaâ metallurgiâ. Bûlletenʹ naučno-tehničeskoj informacii

Author:

Iskakov I. F.¹,Kunitsyn G. A.¹,Lazarev D. V.¹,Red`kin А. А.¹,Trubitsyn S. A.¹,Kharchenko A. S.²

Affiliation:

1. JSC "Ural steel"

2. Magnitogorsk State Technical University after G.I. Nosov

Abstract

To use effectively internal raw material base, JSC “Ural Steel” accomplished I category major overhaul of the blast furnace No. 2. The main purpose of the overhaul was to design a rational profile which could ensure an ability to operate with a charge containing 95 % of Mikhailovskii GOK (mining and concentrating plant) pellets having basicity of 0.5 by CaO/SiO2. The blast furnace No. 2 having useful volume of 1232 m3, was constructed by design of Danieli Corus, the Netherlands, and was blown in on December 30, 2020. In the process of guarantee tests, step-by-step increase of Mikhailovskii GOK pellets (Fetotal = 60.5 %, CaO/SiO2 = 0.5) content in the charge iron ore part was being accomplished from 55 to 95.1%. Charging of the blend containing pellets in the amount of 55% of iron ore part, was done by charging system 4OOCC + 1COOCC (Ore - Coke) with filling level 1.5 m. Under conditions of pellets part increase in the blend, the charging system was changed to decrease their content at the periphery, to increase it in the ore ridge zone and make it intermediate between periphery and the ore ridge. At the pellets share in the iron ore raw materials 0.75 the charging system was used as the following: 3OOCC + 1COOC + 1COOCC, while at the content 95.1% the following charging system was used: 2COOC + 2COOC + 1COOCC. It was noted that in the period of guarantee tests the furnace running was smooth. The average silicon content in the hot metal was 0.70% at the standard deviation 0.666. Sulfur content in the hot metal did not exceed 0.024%, the blowing and natural gas consumption figures were 2100 m3/min and 11000 m3/min correspondently, oxygen content in the blowing 26.5%, hot blowing and top smoke pressure figures were 226.5 and 109.8 KPa correspondently. The productivity of the furnace was reached as high as 2358 t/day at the specific coke rate 433 kg/t of hot metal. After guarantee tests completion, the pellets content in the iron ore part was decreased gradually from 95 down to 50%. The decreasing was made by 5% in every 6 hours of operation. Application of the mastered technology of the blast furnace No. 2 with the increased share of pellets will enable to stably supply the blast furnaces No. 1, 3 and 4 by iron ore raw materials in the proportion of 30-35% of pellets and 65-70% of sinter.

Publisher

JSC Chermetinformatsia

Reference29 articles.

1. Vinogradov E. N., Kal’ko A. A., Volkov E. A. etc. Improvement of smelting technology in domain production of PJSC “Severstal”. Stal’, 2016, no. 1, pp. 16-21. (In Russ.).

2. Sibagatullin S. K., Kharchenko A. S., Beginyuk V. A., Selivanov V. N., Chernov V. P. Improvement of the blast-furnace process by increasing the consumption of natural gas in gas dynamics in the upper stage of heat transfer. Vestnik MGTU im. G. I. Nosova, 2017, no. 1, pp. 37-44. (In Russ.).

3. Sibagatullin S. K., Kharchenko A. S., Chernov V. P., Beginyuk V. A. Improvement of blast furnace practice due to creation of the conditions for elevation of natural gas consumption via usage of raw materials with increased strength. Chernye metally, 2017, no. 8, pp. 27-33. (In Russ.).

4. Nekrasov Z. I., Gladkov N. A., Yakovlev Yu. V. etc. Experimental melts with a change in the share of non-fluxed pellets SSGOK in the blast-furnace mine of MMK from 0 to 100%. Stal’, 1978, no. 1, pp. 11-14. (In Russ.).

5. Babarykin N. N., Druzhkov V. G., Gorbunov G. V. O stoikosti kholodil’nikov shakhtdomennykhpechei [On the durability of refrigerators in the mine of blast furnaces]. Proizvodstvo chuguna: Mezhvuz. sb. nauchn. tr. [Production of cast iron: Interuniversity. Sat. scientific works]. Sverdlovsk: UPI, 1979, no. 5, 202 p. (In Russ.).