Affiliation:
1. School of Chemistry and Biological Engineering, Changsha University of Science and Technology , Changsha , China
Abstract
Abstract
The corrosion behavior of 15CrMo used for water-wall tubes was studied in various urea-containing solution to determine the corrosion problem of water-wall tubes caused by urea in a coal-fired power plant. Urea decomposition tests, together with corrosion experiments, were carried out. The temperature was 320 °C, and the concentrations of urea were 70, 140, 280, 560 and 840 mg/L. Weight loss experiments and surface analysis indicated that the corrosion of 15CrMo steel is mainly manifested as localized corrosion. The corrosion rate of 15CrMo steel increased with the increase of urea concentration, and the maximum value reached 0.686 mm/y (mm per year) when the urea concentration was 840 mg/L. Electrochemical analysis suggested that the corrosion rates of 15CrMo were enhanced substantially by urea decomposition products. The results of UPLC-ESI-MS, infrared spectroscopy and X-ray diffraction showed that urea solution produced corrosive ions NH2COO− during the decomposition process, which caused the corrosion of 15CrMo. Results provided evidence as relevant explanation for the corrosion behavior of 15CrMo in urea solution.
Funder
Hunan Provincial Science and Technology Plan Key Project
Subject
General Materials Science,General Chemical Engineering,General Chemistry
Reference40 articles.
1. Bacsik, Z., Ahlsten, N., Ziadi, A., Zhao, G., Garcia-Bennett, A.E., Martín-Matute, B., and Hedin, N. (2011). Mechanisms and kinetics for sorption of CO2 on bicontinuous mesoporous silica modified with n-propylamine. Langmuir 27: 11118–11128, https://doi.org/10.1021/la202033p.
2. Bacsik, Z. and Hedin, N. (2016). Effects of carbon dioxide captured from ambient air on the infrared spectra of supported amines. Vib. Spectrosc. 87: 215–221, https://doi.org/10.1016/j.vibspec.2016.10.006.
3. Bagchi, A., Gope, D.K., Chattopadhyaya, S., and Wuriti, G. (2020). A critical review on susceptibility of stress corrosion cracking in maraging steel weldments. Mater. Today 27: 2303–2307, https://doi.org/10.1016/j.matpr.2019.09.117.
4. Bernhard, A.M., Peitz, D., Elsener, M., Wokaun, A., and Kröcher, O. (2012). Hydrolysis and thermolysis of urea and its decomposition byproducts biuret, cyanuric acid and melamine over anatase TiO2. Appl. Catal. B Environ. 115–116: 129–137, https://doi.org/10.1016/j.apcatb.2011.12.013.
5. Çömlekçi, G.K. and Ulutan, S. (2018). Encapsulation of linseed oil and linseed oil based alkyd resin by urea formaldehyde shell for self-healing systems. Prog. Org. Coating 121: 190–200.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献