Impact strength of surface treated SS316L wires reinforced PMMA**

Abstract

Abstract Stainless steel 316L (SS316L) as a significant bio-material, their wires were used to support the PMMA matrix. Two simple and low-cost surface pretreatments for SS316L wires were performed to enhance denture impact strength: mechanical scratching (treating SS316L wires with SiC powder inside a rotating container) and electrochemical anodizing. Three mechanical scratching samples for different periods of 60, 90 and 120min were prepared. Anodizing technique conditions were: Ethylene glycol with perchloric acid as an anodizing solution, 15V supplying and graphite rod as an anode. Anodizing process involved three pretreating periods of 15, 20, and 30min. All the prepared samples had dimensions of 65 × 10 × 3 mm. SEM technique showed different morphology nature involved holes, scratches and pores with a density of 104/μm2 and a crack length of 60μm. The PMMA reinforced with scratched stainless steel 316L wire surface for 120 min presented the highest impact strength value (42 kJ/m2) with (450.91%) increment. Anodizing samples showed a fluctuating behavior of samples with enhancing in the impact strength of anodizing wire for 20min of about 26.99 kJ/m2, which is still lower than that for scratched samples in average.