Segregation of Elements in Continuous Cast Carbon Steel Billets Designated for Long Products

Abstract

Abstract This article presents research results concerning designation of the scope of segregation of elements by analysing the ingot, designated for hot rolling of long products. The research tests were performed under industrial conditions, during continuous casting production cycle of high carbon steels. From cc ingots with square cross-section of 160 mm samples having the length of 400 mm were collected, out of which two samples were cut up, the so-called templates with the thickness of 20 mm. Segregation of elements was determined based on the quantitative analysis of results performed by using spark spectrometry pursuant to PN-H-04045. Changes in concentrations of elements were analysed along the line, which join the opposite sides of the sample in their half length and pass through the geometric centre of the square cross-section. In the further course of the research study, there was also determined the segregation along perpendicular line up to the surface connecting the core of the cross-section with lateral plane. Designations of element contents were performed at points distanced from each other by approx. 10 mm and situated on the lines. There was found segregation of carbon, sulphur and phosphorus.