Abstract
AbstractThe influence of cooling rate after homogenization on the 2017A alloy microstructure was analysed. The capability of the θ (Al2Cu) particles, precipitated during various homogenization coolings, for rapid dissolution was estimated. For this purpose, the DSC test was used to determine the effect of the cooling rate after homogenization on the course of melting during a rapid heating. Moreover, the samples after solution heat treatment (with short time annealing) and ageing, were subjected to the microstructure investigations and the microhardness of grains interiors measurements. It was found that cooling after homogenization at 160 °C/h is sufficient for precipitation of fine θ phase particles, which dissolve during the subsequent rapid heating. The cooling at 40 °C/h, causes the precipitation of θ phase in the form of large particles, incapable of further fast dissolution.
Reference13 articles.
1. of th International Aluminum Extrusion Technology Seminar;Dixon;Proc,2000
2. Comparaison des donnees de trempe, determinees a l'aide d'une methode numerique, a celles du regime permanent
3. of th International Aluminum Extrusion Technology Seminar vol;Reiso;Proc,1996
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献