The paper presents a study on corrosion behaviour and tribological properties of nickel composite coatings deposited by electrochemical method on aluminium alloy from 2xxx series (AlCu4MgSi). The nickel composite coatings were produced in a Watts bath of the following chemical composition: NiSO4·7H2O 150 g/l, NiCl2·6H2O 30 g/l, H3BO3 30 g/l with the addition of saccharin in an amount of 2 g/l. As hard ceramic dispersed particles embedded in the coating, alumina (Al2O3) was used in an amount of 12,5; 25; 50 and 75 g/l. Coatings were produced using cathodic current density of 6 A/dm2, bath temperature of 60°C, pH 4, and the time 60 minutes. The electroplating bath was stirred with a mechanical stirrer (350 rpm).
The results obtained were compared with a nickel coating deposited without the ceramic particles. It was found that the presence of Al2O3 increases the wear resistance of composite coatings, but does not significantly improve the corrosion properties.
Reference3 articles.
1. of Metallurgy and Materials;Karaś;Archives,2014
2. Synthesis and properties of electrodeposited ceria nanocomposite coatings Surface;Aruna;Coatings Technology,2006
3. Corrosion and wear resistance properties of composite coatings containing various forms of alumina;Aruna;Appl Electrochem,2011
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献