Physical and mechanical response of porous metals composites with nano-natural additives

Author:

Hassan Zainab Kassim1,Kseer Khamaal Mohsin2

Affiliation:

1. Department of Applied Science, University of Technology , Baghdad , Iraq

2. Department of Mechanical Engineering, College of Engineering, Wasit University , Wasit , Iraq

Abstract

Abstract The mechanical and physical characteristics of composites are made of reinforced palm leaves and copper, the green palm leaves in nanoparticles forms once, and another sample from ash powder of palm leaves with copper powder metal as a matrix that was studied. First, a Cu metal was complemented with green palm leaf at a ratio (10:20:30)% on a sub-micron scale and second with the ash of palm leaves with the same ratio (10, 20, and 30)% and as nanoparticles. Apparent porosity, thermal conductivity, SEM, and compressive strength were carried out. It was noticed that adding additives to Cu causes its apparent porosity rise, porosity value of Cu samples supported with green palm leaves fibers was higher than that of Cu samples supported with palm leaves ash, and the highest percent of porosity was for the sample supported with 30% green palm leaves fibers which were 2.4%. It is also clear from the results that the increase in the percentage of additives led to a significant decrease in the thermal conductivity, as it decreased from 385 W/m K for the unsupported copper sample to 175 W/m K for the green copper supported sample, which was the lowest value, while the lowest value recorded for the palm leaves ash supported sample was 253 W/m K. The results of the compression test showed that the inverse relationship between the percentage of additives and the value of the compressive strength, as the lowest value of the compressive strength estimated at 23 MPa was recorded for the copper sample reinforced with 30% green palm leaves, and it is the same sample that recorded the highest value for porosity as mentioned before.

Publisher

Walter de Gruyter GmbH

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3