Research on vacuum brazing of W-Cu composite to stainless steel with Cu-Mn-Co brazing metal

Author:

Liang Qiuhui1,Xia Chunzhi1,Xu Xiangping1,Zou Jiasheng1

Affiliation:

1. 1Provincial Lab of Advanced Welding Technology, Jiangsu University of Science and Technology, Zhenjiang 212003, China

Abstract

AbstractThis thesis is a discussion on obtaining a vacuum brazing joint of W-Cu alloy and 18-8 stainless steel with Cu-Mn-Co filler metal under the process parameter of a brazing temperature of 1060°C and holding time of 1 h. Four-point bending strength was tested at room temperature. Microstructure, microhardness, and element distribution near the interface of the brazed seam were observed via micro sclerometer, scanning electron microscope (SEM), and energy disperse spectroscopy (EDS) methods. Finally, analysis of the existence for phase composition near the interface was conducted using X-ray diffraction. Corresponding to a four-point bend strength of 780 MPa, there was a plain-interface, dense microstructure without obvious microdefects that formed. Microhardness values increased near the interface of the brazed joint and decreased gradually to the center of the brazed seam. Element distribution indicated that elements (Cu, Mn, Co) from the filler metal diffused into the interface or even substrates, and Fe and Cu element, together with a little of W element, from the substrates dissolved into the brazed seam region. Fracture morphology of the W-Cu/18-8 steel joint was identified as a mixed feature of fracture type. Moreover, the brazing seam contained mainly a Cu-rich phase, W0.4Cu0.6, α-Fe, and simple substance of W, together with a little of Co0.7Fe0.3.

Publisher

Walter de Gruyter GmbH

Subject

Materials Chemistry,Ceramics and Composites

Reference24 articles.

1. Proceeding of the rd Soldering Conference San;Hiraoka;International USA,2006

2. Berichte;Inoue,2004

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3