AbstractThe cylindrical samples of TC4 titanium alloy prepared by spark plasma sintering (SPS) were compressed with hot deformation of 70% on the thermosimulation machine of Gleeble-1500. The temperature of the processes ranged from 850°C to 1,050°C, and the strain rates varied between 0.001 and 5 s−1. The relative density of the sintered and compressed samples was measured by the Archimedes principle. During hot deformation, the microstructure of the sample was observed. The results show that the average relative density of the samples was 90.2% after SPS. And the relative density was about 98% after the hot deformation of 70%. Under high temperature (>950°C), the sensitivity of flow stress to temperature was reduced. At low strain rate (0.001 s−1), the increase in the deformation temperature promoted the growth of dynamic recrystallization (DRX). At the same temperature, the increase in strain rate slowed down the growth of DRX grains. And the variation tendency was shown from the basket-weave structure to the Widmanstätten structure at a low strain rate (<0.1 s−1), with increase in the strain rate.
Subject
Physical and Theoretical Chemistry,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference38 articles.
1. Microstructure and mechanical properties of Ti-6Al-4V prepared by spark plasma sintering;Heavy Machinery,2017
2. High-strength Ti–6Al–4V with ultrafine-grained structure fabricated by high energy ball milling and spark plasma sintering;Materials Science and Engineering A,2013
3. Effect of temperature on hydrogen absorption characteristic and microstructural evolution of TC21 alloy;Journal of Alloys and Compounds,2015
4. Bulk nanostructured Ti–45Al–8Nb alloy fabricated by cryomilling and Spark Plasma Sintering;Journal of Alloys and Compounds,2019
5. Status quo and development tendency on the research of low cost titanium alloy;Materials Review,2017
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献