Tensile shear strength of UF- and MUF-bonded veneer related to data of adhesives and cell walls measured by nanoindentation

Author:

Stöckel Frank,Konnerth Johannes,Kantner Wolfgang,Moser Johann,Gindl Wolfgang

Abstract

Abstract The tensile shear strength of veneer lap joints was characterised. The joints were produced with an Automated Bonding Evaluation System (ABES) using urea-formaldehyde (UF) as well as melamine-urea-formaldehyde (MUF) adhesive formulated for particleboard production. At a fixed heating temperature of 110°C, a systematic increase in bond strength was observed for both adhesives with increasing cure time. The absolute bond strength was significantly higher for MUF compared to UF. Nanoindentation experiments with the same specimens used for ABES revealed a very hard, stiff and brittle character of the UF resin, whereas the MUF proved significantly less hard and stiff, and less brit-tle. Wood cell walls in contact with adhesive, i.e., where adhesive penetration into the cell wall was assumed, showed significantly altered mechanical properties. Such cell walls were harder, stiffer and more brittle than unaffected reference cell walls. These effects were slightly more pronounced for UF than for MUF. Comparing UF and MUF, the micro-mechanical properties of cured adhesive and interphase cell walls confirm earlier observations that tougher adhesives can lead to higher macroscopic bond strength. In strong contrast to that, no obvious correlation was found between micromechanical properties and the strong cure time dependence of macroscopic bond strength.

Publisher

Walter de Gruyter GmbH

Subject

Biomaterials

Cited by 33 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3