Thermo-Mechanical Processing of Rapidly Solidified 5083 Aluminium Alloy - Structure and Mechanical Properties

Abstract

AbstractAluminium-magnesium 5083 alloy was rapidly solidified by means of melt spinning technique and plastically consolidated during subsequent hot extrusion process. As a result, rods 8 mm in diameter were obtained. Structure of as-extruded material is characterized by ultra-fined grains, which influences on increasement of mechanical properties of the material. The strengthening effect was further enhanced by application of thermo-mechanical treatment consist of cold rolling combined with isothermal annealing. As a result, reduction of grain size from ∼710 nm to ∼270 nm as well as enhancement of yield stress (330 MPa to 420 MPa) and ultimate tensile strength (410 MPa to 460 MPa) were achieved. Based on received results Hall-Petch coefficients (σ0, k) for 5083 RS material were determined.