Sinteraustempering Of Two Mo-(Cu)-(Cr)-(Ni)-(Mn)-C Steels In A Semi-Closed Container In Flowing Nitrogen

Author:

Fiał Ch.,Dudrova E.,Kabatova M.,Kupkova M.,Selecka M.,Sułowski M.,Ciaś A.

Abstract

Abstract Three types of heat treatment, sinteraustempering in 500°C, 400°C and 350°C; sinterhardening and sintering with cooling at the rate 10K/min) as the final operation, on steels sintered semi-closed container were investigated. Results of mechanical properties, microstructure investigations and fracture and EDX analyses are reported. The study involved two PM steels: DH-1 (Fe-2%Cu-1.5%Mo-0.5%C) and 34HNM (Fe-0.2%Mo-0.8%Mn-1.5%Cr-1.5Ni-0.4%C). Prealloyed Höganäs DH (Direct Hardening) iron powder and graphite powder (grade C-UF) were used to produce DH-1 steel. Prealloyed Astaloy CrL iron powder, low carbon ferromanganese, elemental nickel and graphite grade C-UF powder were the starting powders of 34HNM steel. Pressing was in rigid dies at 660MPa according to PN-EN ISO 2740 standard. After compaction, green compacts were sintered in a specially designed semi-closed container at 1120°C for 60 minutes in a nitrogen atmosphere. The chemical composition of the sintering atmosphere was modified by adding ferromanganese and/or activator into the container. All specimens were tested for tensile strength (UTS), elongation (A), yield offset strength (R0,2), TRS, apparent surface and cross section hardness (HV 30). The best combination of strength and plasticity for both steels was achieved after sinteraustempering at 500°C. The results show that, using the specially designed semi-closed container, sinteraustempering in N2 atmosphere offers the same or even better mechanical properties in comparison with sinteraustempering in vacuum. It means that sinteraustempering in N2 atmosphere is a very interesting process in terms of cost in comparison with vacuum sinteraustempering.

Publisher

Walter de Gruyter GmbH

Subject

Metals and Alloys

Reference6 articles.

1. Vacuum heat treatment of components for automotive applications;Girardini;Metallurgia Italiana,2006

2. Effects of Post - Sintering Cooling on the Properties of Low Alloy Sintered Materials in and Particulate Materials;Gagne;Advances Powder Metallurgy,1991

3. A Superior Sinter - Hardenable Material in and Particulate Materials;Baran;Advances Powder Metallurgy,1999

4. A novel method of sintering hybrid steels in an improved semiclosed container system of;Ciaś;Science Sintering,2013

5. Effect of austempering conditions on the microstructure and tensile properties of low alloyed sintered steel Metallurgical and Materials;Campos;Transactions,2010

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3