Liu Qi,Luo Wei,Zhou Shengtai,Zou Huawei,Liang Mei
Abstract
Abstract
The friction and wear properties of polyoxymethylene/polytetrafluoroethylene (POM/PTFE) composites were investigated by using a block-on-ring friction tester and special focus was paid to the effect of weight average molar mass (Mw) of POM. To study the thermodynamic characteristics and wear mechanism of composites, differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) were used. Results showed that friction and wear properties of the composite blends were strongly affected by the Mw of POM and the loading fractions of PTFE. POM/PTFE composites with lower Mw of POM owned better wear resistance abilities under a high-speed sliding regime, which resulted from the effective lubrication of transferred wear debris under a relatively high sliding speed. However, the transfer layer on the counterface could be easily peeled off under the low sliding speed, resulting in higher wear rate of POM/PTFE composites with lower Mw of POM. POM and its composites with high Mw showed comparative high friction levels, related to the strong adhesion between the resin and the steel counterpart. DSC analysis showed that POM with lower Mw had higher crystallinity, which was beneficial to the improvement of wear resistance in a high-speed sliding condition.
Subject
Materials Chemistry,Polymers and Plastics,General Chemical Engineering
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献