Author:
Demiray Yeliz,Yücel Onuralp
Abstract
AbstractIn this study crown magnesium produced from Turkish calcined dolomite by the Pigeon Process was refined and corrosion tests were applied.By using factsage thermodynamic program metalothermic reduction behavior of magnesium oxide and silicate formation structure during this reaction were investigated. After thermodynamic studies were completed, calcination of dolomite and it's metalothermic reduction at temperatures of 1473 K, 1523 K and within a vacuum (varied from 20 to 200 Pa) and refining of crown magnesium was studied. Different flux compositions consisting of MgClConsiderable amount of iron was transferred into the sludge phase and its amount decreased from 0.08% to 0.027%. This refined magnesium was suitable for the production of various magnesium alloys. As a result of decreasing iron content, minimum corrosion rate of refined magnesium was obtained 2.35 g
Subject
Physical and Theoretical Chemistry,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献