Influence of Thermal Ageing on Microstructure and Tensile Properties of P92 Steel

Author:

Sakthivel T.1,Selvi S. Panneer1,Parameswaran P.1,Laha K.1

Affiliation:

1. Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam603102, India

Abstract

AbstractMicrostructure and tensile properties of P92 steel in the normalized and tempered, and thermal aged at 923 K for 5000 h and 10,000 h conditions have been investigated. Laves phase precipitate was observed in the thermal-aged steels. The size of Laves phase precipitate increased with increase in thermal exposure. This was also confirmed from the observation that the area fraction of Laves phase precipitate was higher in the 5000 h aged condition which decreased with further increase in thermal exposure. On the other hand, the size and area fraction of M23C6 precipitate were found increased in the 5000 h aged steel, further continued to enhanced precipitation of fine M23C6 in the 10,000 h aged steel. This resulted in significant increase in area fraction and comparable size with the steel aged for 5000 h. Hardness of the steel was decreased with increase in the duration of ageing. Thermal-aged steels exhibited lower yield stress, ultimate tensile strength and relatively higher ductility in comparison with steel in the normalized and tempered condition. The increase in lath width and recovery of dislocation structure under thermal-aged condition resulted in lower tensile strength and hardness. An extensive Laves phase formation and coarsening by loss of tungsten in the matrix led to decrease in the tensile strength predominantly in the 5000 h aged steel. The tensile strength of 10,000 h aged steel was comparable with that of 5000 h aged steel due to enhanced precipitation of fine M23C6 in the steel due to enhanced mobility of carbon in the absence of tungsten in the matrix.

Publisher

Walter de Gruyter GmbH

Subject

Physical and Theoretical Chemistry,Mechanics of Materials,Condensed Matter Physics,General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3