Raman spectroscopy and microwave dielectric properties of Sn substituted SrLa4Ti5O17 ceramics

Abstract

Abstract SrLa4Ti5−xSnxO17 (0 ≤ x ≤ 2) ceramics were fabricated through solid state ceramic route and their microwave dielectric properties were investigated in an attempt to tune their temperature coefficient of resonant frequency (τf) to zero. The compositions were sintered to single phase SrLa4Ti5O17 and SrLa4Ti4.5Sn0.5O17 ceramics at x = 0 and x = 0.5, and SrLa4Ti4−xSnxO17 along with a small amount of La2Ti2O7 at x = 1. The major phase observed at x = 2 was La2Ti2O7 but along with SrLa4Ti4SnO17 and SrLa4Ti4O15 as the secondary phases. τf decreased from 117 to 23.0 ppm/°C but at the cost of dielectric constant (εr) and quality factor multiplied by resonant frequency (Qufo) which decreased from 65 to 33.6 and 11150 to 4191 GHz, respectively. The optimum microwave dielectric properties, i.e. τf = 38.6 ppm/°C, εr = 45.5 and Q u fo = 7919 GHz, correspond to the SrLa4Ti5−xSnxO17 composition with x = 1.