Degradation Characteristics of Intermetallic Coating on Nickel Base Superalloy Substrate in Gas Ttairbine Blade-Reference-Cited by-同舟云学术

Degradation Characteristics of Intermetallic Coating on Nickel Base Superalloy Substrate in Gas Ttairbine Blade

Published:1995-09 Issue:5 Volume:10 Page:987-1005
ISSN:1042-6914
Container-title:Materials and Manufacturing Processes
language:en
Short-container-title:Materials and Manufacturing Processes

Author:

Sugita Y.,Ito M.,Isobe N.,Sakurai S.,Gold C. R.,Bloomer T. E.,Kameda J.

Publisher

Informa UK Limited

Subject

Industrial and Manufacturing Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science

Link

http://www.tandfonline.com/doi/pdf/10.1080/10426919508935084

Reference15 articles.

1. Viswanathan , R. , and J. M. Allen , eds. Life Assessment and Repair Technology for Combustion Turbine Hot Section, Components , ASM International , Materials Park , OH , ( 1990 ) .

2. Thermomechanical Fatigue Behavior of Materials

3. Advanced Surface Coatings: a Handbook of Surface Engineering

Cited by 8 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Mechanical and thermal properties of nanocarbon-reinforced aluminum matrix composites at elevated temperatures;Composites Part B: Engineering;2016-12

2. Advanced burner-rig test for oxidation–corrosion resistance evaluation of MCrAlY/superalloys systems;Surface and Coatings Technology;2006-12

3. Crack initiation and propagation in air plasma sprayed thermal barrier coatings, testing and mathematical modelling of low cycle fatigue behaviour;Materials Science and Engineering: A;2004-08

4. Measurement of the ductile-to-brittle transition temperature in a nickel aluminide coating by a miniaturised disc bending test technique;Surface and Coatings Technology;2003-02

5. Oxidation/Carbonization/Nitridation and In-Service Mechanical Property Degradation of CoCrAlY Coatings in Land-Based Gas Turbine Blades;Journal of Thermal Spray Technology;1999-09-01